High Temperature Coating Mater

  • Product Name: High Temperature Resistant Coating Material

Product overview

High temperature resistant coating material is a protect agent coated on the surface of hot components such as the burning tank of jet plane and the flame tank of bombing plane. The material is of high resistant to heat and oxidation, and can prevent the components from being eroded by high temperature airflow, thereby ensure their working performances and lifetimes. In addition, it is also can be used on some high temperature or insulated components for insulation.

Main Properties and Performance
Type Highest Operation Temperature（℃） Long-time Service Temperature（℃） Thermal Shock Resistance Bending Suitable Substrate
 
W-2 1100 1050 does not peel after quickly quenching from 1200℃to 20℃in water for 6 times
 		 no failure after 30° bent test
 		 nickel-based superalloy
 
B-1000 1000 950 does not peel after quickly quenching from 1050℃to 20℃in water for 6 times
 		 iron-based and nickel-based superalloy
 
A-418 1000 900 does not peel after quickly quenching from 1050℃to 20℃in water for 6 times
 		 iron-based and nickel-based superalloy
424 1050 950 does not peel after quickly quenching from 1050℃to 20℃in water for 6 times nickel-based superalloy
 
536 1050 1050 does not peel after quickly quenching from 1150℃to 20℃in water for 6 times
 		 nickel-based superalloy
 
GT-6 1000 950 does not peel after quickly quenching from 1150℃to 20℃in water for 6 times
 		 nickel-based superalloy